Recycled Pp Granules Black Color
Recycled Polypropylene PP Granules
Post-industrial recycled PP granules.
Recycled PP granules from thermoformed food contact containers.
High quality, produced only from industrial sources.
Colour: Black
Melt Flow Index: 3-4 g/10min
Loading weight: 24-25 Tonnes
Packaging,: Big-bags
Related products
abs-novodur
novodur regrind
thin lack
HDPE Pallet Regrinds
Ongoing loads of HDPE Pallet regrinds – no HMW but a small amount of PP will be within
Melt 2-5
PVC Cable Regrind Mixed Color Plastic Scrap Material
PA Mix
PA 80%- PP/POM 20% mix regrind
Yarn

|
item
|
value
|
|
Feature
|
Moisture-Absorbent, Anti-pilling, Recycled
|
|
Yarn Type
|
Cotton, Polyester
|
|
Use
|
For knitting sock gloves towel…
|
|
Yarn Count
|
NE1/16
|
|
Model Number
|
J0011
|
|
Color
|
Customized Color
|
|
Twist
|
<650TPM
|
|
Strength
|
>250CN
|
|
Place of Origin
|
Zhejiang, China
|
|
Material
|
Polyester / Cotton
|
EPE Hot Melt Blocks
30,000lbs EPE Hot Melt Blocks
PA6 Natur regrind
PVC From Pipes
Long Service Life Pvc Particles Nice Price Pvc Particles High Elastic And Environmentally Pvc Particles
Pvc Suspension K67 Wet 30% Max
PVC RESIN SUSPENSION WET AT 25% MAX
prime resin was stored outside and took the rain
very good materials
white
1000lb bales of combined #1 and #2 plastics
PET or PETE 1 is a common type of plastic used for packaging. It is transparent, lightweight, strong, and has good barrier properties. PET is easily recyclable and is commonly used for beverage bottles and food containers. It is not recommended to reuse disposable PET drinking bottles.
Carbon Black
High Grade Carbon black. No CC. Carbon 70% USAGE less than 1% Shinny and Black Suitable use for pelletized: ABS / PS / PP / HDPE etc
PE 80+100 Repro
Free Sample High Density Polyethylene Resin HDPE PE100 Virgin HDPE Granules recycled virgin HDPE resin
|
Film Grade HDPE
|
||||
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
|
Density
|
ISO 1183
|
0.944-0.955
|
g/cm3
|
|
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
0.03-0.07
|
g/10min
|
|
Tensile Strength at Yield
|
ISO 527-2
|
22
|
MPa
|
|
|
Elongation at break
|
ISO 527-2
|
>350
|
%
|
|
|
ESCR
|
F50,50°C,100%
|
ASTM D-1693A
|
1000
|
h
|
|
VICAT
|
ASTM D-1525
|
126
|
°C
|
|
|
Blowing molding Grade HDPE
|
||||
|
Item
|
Test Condition
|
Test Method
|
Value
|
Unit
|
|
Density
|
ISO 1183
|
0.950~0.955
|
g/cm
|
|
|
MFR
|
190°C/2.16kg
|
ISO 1133
|
1.7~2.5
|
g/10min
|
|
Tensile strength at Yield
|
ISO 527-2
|
24
|
MPa
|
|
|
Elongation at break
|
ISO 527-2
|
>600
|
%
|
|